2K Custom

2K Metal Grip Base Aerosol Spray Paint

*Please note – These are mixed colours, colour accuracy should be checked before application. No responsibility for colour differences can be accepted after use.

Two-pack acrylic base coat with direct adhesion on non ferrous metal substrates for solid, metallic and mica colours, in a two-coat process. To overcoat with glossy and matt acrylic clearcoat.

Use

General industrial manufactured items.

Characteristics

  • Fast drying
  • Easy application
  • Excellent adhesion on aluminium and its alloys, zama (zinc+aluminium+magnesium), brass and epoxy primers (a previous adhesion test is always recommended)
  • Excellent light resistance
  • Only metallic and mica colours of this basecoat can also be overcoated with soft-touch clearcoat

Substrate Preparation

Aluminium and its alloys, mama (zinc+aluminium+magnesium), brass: degreasing with 00695 silicone remover slow followed by blowing.

Application

Spray – Mixing ratio:

LS945 2K GRIP BASE (derived from binder 29945) 1000 parts

29355 LECHSYS ACRITOP STANDARD HARDENER 100 parts

00825 (Standard) -00824 (Slow) LECHSYS UNIVERSAL THINNERS 500 parts

Pot life at 20°C : 4 hours

Spray viscosity at 20 °C: 16-18” DIN 4

Recommended spray temperature: above 5°C under 30°C

Ø Air cap: 1,2 mm

Air pressure: 3,5 Atm

N° of coats: 2-3

Recommended film thickness: 20-30 μ

Theoretical coverage: 1 kg of mixture = 7.3 mÇ at 25 μ

1 l of mixture = 6.7 mÇ at 25 μ

V.O.C. of the mixture ready for use: ~ 750 g/l

Drying Time

Air drying at 20°C :

Overcoatable with clearcoat after 20 min.

Overcoat With

Acrylic industrial clearcoats for a two-coat process:

96390 ACRIFAN CLEAR COACH

96598 ACRIPLAST CLEAR SEMIOPACA

09852 CERAMIC CLEAR

31575 CLEAR SOFT MATT TH only on metallic and mica colours, NOT on solid colours.